ABSTRACT
Objective@#We aimed to evaluate the cell viability and antimicrobial effects of orthodontic bands coated with silver or zinc oxide nanoparticles (nanoAg and nano-ZnO, respectively). @*Methods@#In this experimental study, 30 orthodontic bands were divided into three groups (n = 10 each): control (uncoated band), Ag (silver-coated band), and ZnO (zinc oxide-coated band). The electrostatic spray-assisted vapor deposition method was used to coat orthodontic bands with nano-Ag or nano-ZnO. The biofilm inhibition test was used to assess the antimicrobial effectiveness of nano-Ag and nano-ZnO against Streptococcus mutans, Lactobacillus acidophilus, and Candida albicans. Biocompatibility tests were conducted using the 3-(4, 5-dimethylthiazol-2-yl)-2, 5-diphenyltetrazolium bromide assay. The groups were compared using oneway analysis of variance with a post-hoc test. @*Results@#The Ag group showed a significantly higher reduction in the number of L. acidophilus, C. albicans, and S.mutans colonies than the ZnO group (p = 0.015, 0.003, and 0.005, respectively). Compared with the control group, the Ag group showed a 2-log 10 reduction in all the microorganisms' replication ability, but only S. mutants showed a 2-log10 reduction in replication ability in the ZnO group. The lowest mean cell viability was observed in the Ag group, but the difference between the groups was insignificant (p > 0.05). @*Conclusions@#Coating orthodontic bands with nanoZnO or nano-Ag induced antimicrobial effects against oral pathogens. Among the nanoparticles, nano-Ag showed the best antimicrobial activity and nanoZnO showed the highest biocompatibility.
ABSTRACT
PURPOSE: The aim of this preliminary study was to investigate, for the first time, the effects of addition of titania nanotubes (n-TiO2) to poly methyl methacrylate (PMMA) on mechanical properties of PMMA denture base. MATERIALS AND METHODS: TiO2 nanotubes were prepared using alkaline hydrothermal process. Obtained nanotubes were assessed using FESEM-EDX, XRD, and FT-IR. For 3 experiments of this study (fracture toughness, three-point bending flexural strength, and Vickers microhardness), 135 specimens were prepared according to ISO 20795-1:2013 (n of each experiment=45). For each experiment, PMMA was mixed with 0% (control), 2.5 wt%, and 5 wt% nanotubes. From each TiO2:PMMA ratio, 15 specimens were fabricated for each experiment. Effects of n-TiO2 addition on 3 mechanical properties were assessed using Pearson, ANOVA, and Tukey tests. RESULTS: SEM images of n-TiO2 exhibited the presence of elongated tubular structures. The XRD pattern of synthesized n-TiO2 represented the anatase crystal phase of TiO2. Moderate to very strong significant positive correlations were observed between the concentration of n-TiO2 and each of the 3 physicomechanical properties of PMMA (Pearson's P value ≤.001, correlation coefficient ranging between 0.5 and 0.9). Flexural strength and hardness values of specimens modified with both 2.5 and 5 wt% n-TiO2 were significantly higher than those of control (P≤.001). Fracture toughness of samples reinforced with 5 wt% n-TiO2 (but not those of 2.5% n-TiO2) was higher than control (P=.002). CONCLUSION: Titania nanotubes were successfully introduced for the first time as a means of enhancing the hardness, flexural strength, and fracture toughness of denture base PMMA.